Studies of the photostability of CdSe/CdS dot-in-rod nanoparticles

Xiaoming Wen*, Amit Sitt, Pyng Yu, Hsien Chen Ko, Yon Rui Toh, Jau Tang

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

Abstract

Fluorescent CdSe/CdS dot-in-rod nanoparticles have attracted considerable interest for fundamental research and potential applications in bioscience and physical science. In this work, we investigated photoinduced phenomena in CdSe/CdS dot-in-rods using time-resolved photoluminescence (PL). Our experimental results show that photopassivation, photooxidation, and photoinduced defect/ surface states occur in CdSe/CdS dot-in-rods, and these processes depend on the irradiation amount. The thickness of the CdS shell plays an important role for photostability. Photopassivation was found to initially result in an increase of PL intensity when fluence is low. Photooxidation was found to cause a spectral blue shift due to shrinkage of the core. We also found that a thick shell of CdS can effectively suppress photooxidation and hinder the diffusion of oxygen into the core. Irradiation could generate defect/surface states predominantly in the shell and also on the interface between the core and the shell. A weak PL shoulder in the blue side was observed in heavily irradiated samples as a result of photoinduced rupture of encapsulation.

Original languageEnglish
Article number1278
JournalJournal of Nanoparticle Research
Volume14
Issue number12
DOIs
StatePublished - Dec 2012
Externally publishedYes

Funding

FundersFunder number
Eshkol Foundation
National Science Council98-2221-E-001-019, 99-2221-E-001-002-MY3
Academia Sinica
Ministry of Science and Technology, Israel

    Keywords

    • CdSe/CdS dot-in-rod
    • Fluorescence
    • Photooxidation
    • Photopassivation
    • Seeded growth

    Fingerprint

    Dive into the research topics of 'Studies of the photostability of CdSe/CdS dot-in-rod nanoparticles'. Together they form a unique fingerprint.

    Cite this