TY - JOUR
T1 - Structural characterization of interfaces in epitaxial Fe/MgO/Fe magnetic tunnel junctions by transmission electron microscopy
AU - Wang, C.
AU - Kohn, A.
AU - Wang, S. G.
AU - Chang, L. Y.
AU - Choi, S. Y.
AU - Kirkland, A. I.
AU - Petford-Long, A. K.
AU - Ward, R. C.C.
PY - 2010/7/28
Y1 - 2010/7/28
N2 - We present a detailed structural characterization of the interfaces in Fe/MgO/Fe layers grown by molecular-beam epitaxy using aberration-corrected transmission electron microscopy (TEM), scanning TEM, and electron energy-loss spectroscopy. When fabricated into magnetic tunnel junctions, these epitaxial devices exhibit large tunnel magnetoresistance ratios (e.g., 318% at 10 K), though still considerably lower than the values predicted theoretically. The reason for this discrepancy is being debated and has been attributed to the structure of, and defects at the interface, namely, the relative position of the atoms, interface oxidation, strain, and structural asymmetry of the interfaces. In this structural study, we observed that Fe is bound to O at the interfaces. The interfaces are semicoherent and mostly sharp with a minor degree of oxidation. A comparison of the two interfaces shows that the top MgO/Fe interface is rougher.
AB - We present a detailed structural characterization of the interfaces in Fe/MgO/Fe layers grown by molecular-beam epitaxy using aberration-corrected transmission electron microscopy (TEM), scanning TEM, and electron energy-loss spectroscopy. When fabricated into magnetic tunnel junctions, these epitaxial devices exhibit large tunnel magnetoresistance ratios (e.g., 318% at 10 K), though still considerably lower than the values predicted theoretically. The reason for this discrepancy is being debated and has been attributed to the structure of, and defects at the interface, namely, the relative position of the atoms, interface oxidation, strain, and structural asymmetry of the interfaces. In this structural study, we observed that Fe is bound to O at the interfaces. The interfaces are semicoherent and mostly sharp with a minor degree of oxidation. A comparison of the two interfaces shows that the top MgO/Fe interface is rougher.
UR - http://www.scopus.com/inward/record.url?scp=77956551597&partnerID=8YFLogxK
U2 - 10.1103/PhysRevB.82.024428
DO - 10.1103/PhysRevB.82.024428
M3 - ???researchoutput.researchoutputtypes.contributiontojournal.article???
AN - SCOPUS:77956551597
SN - 1098-0121
VL - 82
JO - Physical Review B - Condensed Matter and Materials Physics
JF - Physical Review B - Condensed Matter and Materials Physics
IS - 2
M1 - 024428
ER -