Novel approach to space-survivable polyimides: Liquid phase deposition of Titania coating on Kapton

Irina Gouzman*, Olga Gershevitz, Eitan Grossman, Noam Eliaz, Chaim N. Sukenik

*Corresponding author for this work

Research output: Contribution to journalConference articlepeer-review

Abstract

Polyimides are widely used as spacecraft external surfaces materials. They are exposed to atomic oxygen (AO), which is the main constituent of a residual atmosphere at low Earth orbit (LEO) and should be protected from the space harsh environment. This work presents an innovative approach to applying a protective coating on Kapton polyimide using liquid-phase deposition (LPD) and shows its effectiveness in reduction of AO-induced surface erosion. Titania coatings, 100 nm thick, were deposited on Kapton films by LPD using an aqueous solution of a metal-fluoride complex and boric acid at near ambient conditions. Adherent, crack-free, coatings have been obtained by optimization of the deposition conditions, the substrate surface pre-treatment procedure and post-deposition drying. Characterization of the oxide coating included Atomic Force Microscopy (AFM) in tapping and nano-indentation modes, Environmental Scanning Electron Microscopy (ESEM), and X-ray Photoelectron Spectroscopy (XPS). The durability of the titania coating under AO attack was studied using a RF plasma based facility. Surface erosion was measured both gravimetrically and by in situ Quartz Crystal Microbalance (QCM) measurements of mass loss. A dramatic reduction in the erosion of titania-coated Kapton relative to uncoated Kapton was observed: the erosion yield was as low as 2% of that of uncoated Kapton after exposure to 4× 1020 O-atoms-cm-2 of LEO equivalent AO fluence. In addition, the surface hardness of coated Kapton was improved both in the as-deposited titania coatings and in the AO-exposed titania films.

Original languageEnglish
Pages (from-to)391-404
Number of pages14
JournalAIP Conference Proceedings
Volume1087
DOIs
StatePublished - 2009
Event9th International Conference on Protection of Materials and Structures From Space Environment, ICPMSE-9 - Toronto, ON, Canada
Duration: 20 May 200823 May 2008

Fingerprint

Dive into the research topics of 'Novel approach to space-survivable polyimides: Liquid phase deposition of Titania coating on Kapton'. Together they form a unique fingerprint.

Cite this